Description
8012 A,B is a two-component heat curing liquid silicone elastomer, which cures by a poly addition reaction. All Products are specially engineered for coating applications.
|
Properties |
8012A |
8012B |
|
Appearance |
Viscous liquid |
Viscous liquid |
|
Color |
translucent |
translucent |
|
Viscosity (at 23±2 °C, mPas appr.) (Measured with Brookfield viscometer, needle no 7, speed 10rpm) |
200,000 |
100,000 |
|
Mixing the two components |
||
|
8012A |
100 parts |
|
|
8012B |
100 parts |
|
|
Pot life of mixture at 23±2 ℃, hours, approx |
>8 |
|
|
Viscosity of the mix at 23±2 ℃, mPa.s approx |
110,000 |
|
|
Curing time at 160°C measured with rheometer, min, approx |
<1 |
|
|
Mechanical properties of the cured material (Measured after cross-linking 15 min at 150°C + 24hours at 23°C) |
||
|
Shore A hardness, approx |
40 |
|
|
Tensile strength, MPa, approx |
＞5 |
|
|
Elongation at break, %, approx |
＞150 |
|
|
Tear strength, kN/m, approx |
＞25 |
|
- Technical textile coatings
- Industrial and high-performance fabrics
- Artificial leather
- Elastic fabrics
- High bond strength without primer on textiles from different origins.
- Good abrasion and scuff resistance on certain fabrics
- Excellent non-slip properties.
- High elongation
- Long bath life at room temperature (>8 hours).
- Fast cure at elevated temperature.
- Solvent-free system