Description
This resin is composed of phenyl chlorosilicon, methyl chlorosilane, and organosilicon resin, which are reacted using the latest technology.
The resin has excellent heat resistance, weather resistance, oil resistance, solvent resistance, and excellent insulation performance. It can be used regularly at 250 ℃+5 ℃. It has the characteristic of low-temperature drying and can be used for producing high-temperature resistant coatings, H-grade insulation paints, sealing for electrical components, impregnated glass fiber cloth, glass fiber sleeves, enameled wires, metal sheet coils, and other purposes.
|
Code |
Appearance |
Viscosity25℃ |
Solid% |
Dry time |
Heat resistance |
Feature & Application |
|
6804 |
Transparent liquid |
20~40 |
50±2 |
150℃,1.5h |
250 ℃, 200h No cracking No foaming Not falling off
|
This resin has excellent heat resistance, weather resistance, oil resistance, solvent resistance, and good insulation performance, and can be used for a long time at 250 ° C ± 50 ° C. It has the characteristic of low-temperature drying and can be used for producing high-temperature resistant coatings, H-grade insulation paints, sealing for electrical components, impregnated glass fiber cloth, glass fiber sleeves, enameled wires, metal sheet coils, and other purposes. |
|
680E-3 |
Light yellow transparent liquid, allowing for milky white light |
100~250 |
60±2 |
Dry surface for 2 hours Dry at 180 ℃ for 1 hour Bake at 250 ° C for 20-25 minutes Bake at 280 ° C for 0-15 minutes
|
400 ℃ for 4 hours No cracking No foaming Not falling off
|
The latest development of this series of resins is used for non stick pot coatings. Has excellent heat resistance, weather resistance, corrosion resistance, electrical insulation and bending resistance, and high tensile strength; Moreover, the paint film has good fullness, high temperature hardness, and good gloss. Especially with good tactile and non sticky characteristics. Widely used in non stick pots such as fryers, rice cookers, grill racks, barbecue ovens, etc. It can also be used in household appliances, electric heating containers, gas stoves, cookware, etc. |
|
680Z-4 |
Light yellow transparent liquid, allowing for milky white ligh |
150~400 |
60±2 |
Dry surface for 2 hours Dry at 180 ℃ for 1 hour Bake at 250 ℃ for 20-25 minutes Bake at 280 ℃ for 10-15 minutes
|
400 ℃ for 4 hours No cracking No foaming Not falling off
|
The 680Z-4 resin does not discolor the paint film at 280-290 ℃ for 10-15 minutes. And the fullness is good. High gloss, good high-temperature hardness. Reaching 1, with good non stick properties, commonly used for painting in non stick pots, with a thermal hardness of 3H. |
|
680Z-5 |
Dry surface for 2 hours Dry at 180 ℃ for 1 hour Bake at 250 ℃ for 20-25 minutes Bake at 280 ℃ for 10-15 minutes |
400 ℃ for 4 hours No cracking No foaming Not falling off
|
680Z-5 resin has higher temperature resistance, higher gloss, and better non stickiness. Commonly used as an inner coating for rice cookers.。 |
|||
|
650-1 |
Light yellow transparent liquid, allowing for milky white light |
>20 |
50±2 |
Bake at 180 ℃ for 1 hour |
250 ℃, 200h No cracking No foaming Not falling off |
This resin can be formulated into high-temperature coatings at 400-500 ° C. Good hardness, wear resistance, high gloss, suitable for blending various series of high-temperature resistant coatings. Widely used in high-temperature engine exhaust pipes, high-temperature equipment protective insulation coatings, coatings for various household appliances such as electric ovens and ovens, etc. Among them, 650-1 is used in combination with 8812 for better performance. |
|
650-1A |
||||||
|
|
Light yellow transparent liquid, allowing for milky white light |
40~150 |
50±2 |
Dry surface for 15 minutes Bake at 180 ℃ for 1 hour
|
S-4 (250-300 ℃) Slightly yellow after 2 hours, the paint film is intact and has good adhesion
|
This resin can be cured at room temperature, with good adhesion of the paint film, flexibility, and impact resistance, as well as heat resistance, water resistance, corrosion resistance, and weather resistance. Prepare anti-corrosion and weather resistant coatings for large steel components and equipment, trucks, navigation vessels, water buildings, and metal sheet painting, thereby extending the outdoor service life and greatly reducing maintenance costs. |
|
640S-2 |
640S-2 resin is formulated into a clear paint, which can be used as a single component at room temperature for drying and has good weather resistance. And it can withstand high temperatures of 200~250 ° C for a long time. When formulated into aluminum powder paint, it can withstand high temperatures of 350~450 ° C. |
|||||
|
640S-4 |
|
|
|
|
|
640S-4 resin can be mixed into various colors of organic silicon paint at around 400 ° C, and can be used to adjust the surface of aluminum powder paint at around 500 ° C. The paint film dries quickly and has good hardness, making it suitable for single filament paint. |
1. The resin should avoid contact with acids, alkalis, organic salts, amines, and other substances during use, otherwise it may accelerate curing, gelation, and other phenomena, which will affect the performance of the product.
2. The diluent used in this resin must not contain water, sulfides, or other impurities, otherwise it will affect adhesion, dryness, and other properties.