Description
The solvent-free silicone resin series products are reactive, methylphenyl polysiloxane resins with a narrow molecular weight distribution. It has good compatibility with various organic resins (polyester, acrylic acid, alkyd, epoxy) and can participate in grafting reactions to improve the temperature and weather resistance of organic resins. It can also be used alone to prepare high-temperature anti-corrosion coatings, baking utensils and cookware coatings. The resin has high gloss, good fullness, and high hardness.
|
Code |
Appearance |
Polysiloxane content % |
Viscosity 25℃ (maps) |
Densityg/m³ |
Feature |
|
SR2000 |
Water white or slightly yellow transparent liquid |
≥90 |
80-150 |
1.14 |
Moisture curing (40% -60% moisture), can also be combined with 1-3% titanium ester as a crosslinking reaction, with low smoke during high-temperature baking. |
|
SR2037 |
Water white or slightly yellow transparent liquid |
285 |
200-300 |
1.15 |
FJN-1038 can be used alone or combined in the polyester modification process to improve crosslinking density and thermal hardness. |
|
SR2038 |
Water white or slightly yellow transparent liquid |
≥85 |
250-400 |
1.2 |
Can be used alone or combined with FJN-1000 to prepare moisture curing coatings. |
Notes:
1. Long term storage temperature ≤ 40 ℃, be careful to mix impurities after opening.
2. Avoid contact with acid, alkali and organic curing agent to avoid gel.
3. If the addition ratio of metal drying agents (such as zinc, tin, titanium, zirconium, etc.) exceeds the limit, they must be used up within 24 hours.