High Temperature Methyl Phenyl Silicone Resin

Code

Appearance

Visocsity25℃ (coat 4 cup)S

Sold content%

Dry time

Heat Resistance                            Features & Application

8812

Colorless to light yellow transparent liquid

30~60

50±2

Dry surface for 2h

Practical work for 24 hours

300 ℃± 5 ℃

3 hours

No foaming

No cracking

No color change

Not falling off

This resin series has excellent high-temperature resistance and can be used for a long time at 300C ± 5 ° C. The resin has good hardness, fast drying, and can be combined with organic resins such as alkyd, acrylic acid, and epoxy to prepare various high-temperature resistant coatings for different purposes. H-grade insulation paint and various high-temperature release agents can also be prepared.

8813 resin can be combined with organic silicone resin to form a heat-resistant coating with a heat resistance of 200-800 ℃. The paint film has good hardness and good drying.

8812R

8813

8813 resin can be formulated into a heat-resistant coating with a heat resistance of around 600~800 ℃. The paint film is dry, adheres well, and has good flexibility.

8813-A

8813-A resin can be formulated into a glossy heat-resistant coating with a heat resistance of 400~500 ℃. Good hardness, high gloss, good adhesion, and low smoke emission. 8813-A has better hardness, higher gloss, and better adhesion than 8813.

8813-B

8813-B resin can be mixed with other organic resins to prepare high-temperature baking organic silicon coatings. Its hardness is higher than 8813-A and its compatibility with organic resins is better.

8813-C

8813-Ccan be used to prepare 400-600 ℃ organic silicon coatings, especially suitable for heating plates and furnace heads, with lower smoke emissions and higher product cost-effectiveness.